Andre Stainless stands out as a top-notch manufacturer and supplier of Stainless Steel U Tubes right in Pulau Ujong, Singapore. They specialize in delivering high-quality tubing solutions tailored for heat exchangers, condensers, and boiler systems. Each tube is crafted with precision and adheres to international standards like ASTM, ASME, and EN. Made from premium stainless steel grades such as 304, 316, and 321, these U Tubes boast exceptional strength and corrosion resistance. Thanks to cutting-edge bending technology and rigorous quality control, Andre Stainless guarantees flawless U-bends with tight radii, uniform wall thickness, and a long lifespan, making them ideal for both industrial and commercial uses.
When it comes to composition, Stainless Steel U Tubes primarily consist of iron, with chromium content between 16–20%. They also include varying levels of nickel, molybdenum, and other alloying elements, depending on the specific grade. These tubes are known for their impressive mechanical properties, showcasing high tensile strength, yield strength, and good elongation. The U-bend design maintains its structural integrity even under intense thermal and mechanical stress, making them perfect for high-pressure and high-temperature settings.
| Size Range | 10 mm OD to 50.8 mm OD |
| Stainless Steel U Tube Outside Diameter | 6.00 mm to 101.60 mm |
| Wall Thickness | 0.70 mm to 8.00 mm |
| Length | up to 20 m (65.62 ft) Length & Customed Required Length |
| Stainless Steel Heat Exchanger Tube Dimenisons | ASTM, AISI, ASME/ ANSI, JIS, DIN, EN, GB, BS, SUS |
| Standard | ASTM A 213, A 268, A 269, A 789, Equivalent to ASME, EN, JIS Etc. |
| Stainless Steel U tube Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | Ti | Fe | |
| 304 | min. | 18.0 | 8.0 | |||||||||
| max. | 0.08 | 2.0 | 0.75 | 0.045 | 0.030 | 20.0 | 10.5 | 0.10 | ||||
| 304L | min. | 18.0 | 8.0 | |||||||||
| max. | 0.030 | 2.0 | 0.75 | 0.045 | 0.030 | 20.0 | 12.0 | 0.10 | ||||
| 304H | min. | 0.04 | 18.0 | 8.0 | ||||||||
| max. | 0.010 | 2.0 | 0.75 | 0.045 | 0.030 | 20.0 | 10.5 | |||||
| SS 310 | 0.015 max | 2 max | 0.015 max | 0.020 max | 0.015 max | 24.00 26.00 | 0.10 max | 19.00 21.00 | 54.7 min | |||
| SS 310S | 0.08 max | 2 max | 1.00 max | 0.045 max | 0.030 max | 24.00 26.00 | 0.75 max | 19.00 21.00 | 53.095 min | |||
| SS 310H | 0.04 0.10 | 2 max | 1.00 max | 0.045 max | 0.030 max | 24.00 26.00 | 19.00 21.00 | 53.885 min | ||||
| 316 | min. | 16.0 | 2.03.0 | 10.0 | ||||||||
| max. | 0.035 | 2.0 | 0.75 | 0.045 | 0.030 | 18.0 | 14.0 | |||||
| 316L | min. | 16.0 | 2.03.0 | 10.0 | ||||||||
| max. | 0.035 | 2.0 | 0.75 | 0.045 | 0.030 | 18.0 | 14.0 | |||||
| 316TI | 0.08 max | 10.00 14.00 | 2.0 max | 0.045 max | 0.030 max | 16.00 18.00 | 0.75 max | 2.00 3.00 | ||||
| 317 | 0.08 max | 2 max | 1 max | 0.045 max | 0.030 max | 18.00 20.00 | 3.00 4.00 | 57.845 min | ||||
| SS 317L | 0.035 max | 2.0 max | 1.0 max | 0.045 max | 0.030 max | 18.00 20.00 | 3.00 4.00 | 11.00 15.00 | 57.89 min | |||
| SS 321 | 0.08 max | 2.0 max | 1.0 max | 0.045 max | 0.030 max | 17.00 19.00 | 9.00 12.00 | 0.10 max | 5(C+N) 0.70 max | |||
| SS 321H | 0.04 0.10 | 2.0 max | 1.0 max | 0.045 max | 0.030 max | 17.00 19.00 | 9.00 12.00 | 0.10 max | 4(C+N) 0.70 max | |||
| 347/ 347H | 0.08 max | 2.0 max | 1.0 max | 0.045 max | 0.030 max | 17.00 20.00 | 9.0013.00 | |||||
| 410 | min. | 11.5 | ||||||||||
| max. | 0.15 | 1.0 | 1.00 | 0.040 | 0.030 | 13.5 | 0.75 | |||||
| 446 | min. | 23.0 | 0.10 | |||||||||
| max. | 0.2 | 1.5 | 0.75 | 0.040 | 0.030 | 30.0 | 0.50 | 0.25 | ||||
| 904L | min. | 19.0 | 4.00 | 23.00 | 0.10 | |||||||
| max. | 0.20 | 2.00 | 1.00 | 0.045 | 0.035 | 23.0 | 5.00 | 28.00 | 0.25 | |||
| Stainless Steel U tube Grade | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 304/ 304L | 8.0 g/cm3 | 1400 °C (2550 °F) | Psi 75000 , MPa 515 | Psi 30000 , MPa 205 | 35 % |
| 304H | 8.0 g/cm3 | 1400 °C (2550 °F) | Psi 75000 , MPa 515 | Psi 30000 , MPa 205 | 40 % |
| 310 / 310S / 310H | 7.9 g/cm3 | 1402 °C (2555 °F) | Psi 75000 , MPa 515 | Psi 30000 , MPa 205 | 40 % |
| 306/ 316H | 8.0 g/cm3 | 1400 °C (2550 °F) | Psi 75000 , MPa 515 | Psi 30000 , MPa 205 | 35 % |
| 316L | 8.0 g/cm3 | 1399 °C (2550 °F) | Psi 75000 , MPa 515 | Psi 30000 , MPa 205 | 35 % |
| 317 | 7.9 g/cm3 | 1400 °C (2550 °F) | Psi 75000 , MPa 515 | Psi 30000 , MPa 205 | 35 % |
| 321 | 8.0 g/cm3 | 1457 °C (2650 °F) | Psi 75000 , MPa 515 | Psi 30000 , MPa 205 | 35 % |
| 347 | 8.0 g/cm3 | 1454 °C (2650 °F) | Psi 75000 , MPa 515 | Psi 30000 , MPa 205 | 35 % |
| 904L | 7.95 g/cm3 | 1350 °C (2460 °F) | Psi 71000 , MPa 490 | Psi 32000 , MPa 220 | 35 % |
Contact us to get a quick quote for your requirement.
Client satisfaction by all means forms the top priority with regard to the quality of our Stainless Steel U Tubes. In pursuit of this objective, all our products are given stringent quality assurance regime, which includes hardness tests, chemical analysis by way of spectro analysis, positive material identification (PMI), flattening tests, micro and macro tests, pitting resistance tests, flaring tests and intergranular corrosion (IGC) tests.
To maintain Stainless Steel U Tubes, regularly clean them with mild soap and water to remove dirt and grime. Avoid harsh chemicals and abrasive cleaners. Inspect for signs of corrosion or damage and address any issues promptly.
Stainless Steel U Tubes are highly resistant to corrosion due to their chromium content. However, under extreme conditions like exposure to harsh chemicals or saltwater, corrosion can still occur over time.
Yes, Stainless Steel U Tubes can be used for natural gas applications. They offer excellent corrosion resistance and durability, making them suitable for handling natural gas in various industrial systems.
In Pulau Ujong, Stainless Steel U Tubes find their place in various applications, including power generation, oil & gas, petrochemical processing, desalination plants, and HVAC systems. They’re commonly utilized in shell and tube heat exchangers, steam condensers, superheaters, and economizers, thanks to their remarkable resistance to corrosion, oxidation, and thermal fatigue. The U-shaped design not only optimizes space but also minimizes thermal expansion stresses and enhances fluid flow. Andre Stainless also provides customized U Tubes, offering precise bend radii, leg lengths, and finishes to cater to the diverse needs of industries across Singapore.